White Solid Wood Hot Glue Sticks Flat Lamination Hot Melt Bonding PUR-9002.1
Product Details:
| Place of Origin: | CHINA |
| Brand Name: | WANLI-ADHESION |
| Certification: | ISO9001 ISO14001 IATF16949 |
| Model Number: | PUR-9002.1 |
Payment & Shipping Terms:
| Minimum Order Quantity: | 20KG |
|---|---|
| Packaging Details: | 2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel |
| Delivery Time: | 5-8 work days |
| Payment Terms: | L/C, T/T |
|
Detail Information |
|||
| Product: | PUR Hot Melt Adhesive | Component: | PUR (Polyurethane) |
|---|---|---|---|
| Appearance: | White / Solid | Solid Content: | 100 Percent |
| Shelf Life: | 6 Months | Melt Viscosity: | Around 6500mPa·s @ 140℃ |
| Operating Temperature: | 130℃～140℃ | Open Time: | 5-6 Minutes |
| Useage Scope: | Flat Lamination Of Plastic Films/Aluminized Films To Wood/Wood-plastic Materials | Application Industry: | PUR Hot Melt Adhesive For Woodworking Flat Lamination Bonding |
| High Light: | white wood hot glue sticks,solid wood hot glue sticks,flat lamination hot melt bonding |
||
Product Description
Factory Direct Supply WANLI® PUR-9002.1 White 100% Solid PUR Hot Melt Adhesive for Flat Lamination Bonding of Plastic Films/Aluminized Films to Wood/Wood-plastic Materials
Wanli® PUR hot melt adhesive PUR-9002.1 for woodworking flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-9002.1 can be used for the lamination of plastic films/aluminized films to wood/wood-plastic materials. PUR-9002.1 has high initial strength and moderate open time. PUR-9002.1 is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final bonding strength. After curing, PUR-9002.1 has good peeling strength, good heat&moisture resistance and chemical resistance.
APPLICATION
Wanli® PUR hot melt adhesive PUR-9002.1 is used for woodworking flat lamination bonding. PUR-9002.1 can be used for the lamination of plastic films/aluminized films to wood/wood-plastic materials.
| Application Material | Decorative Panels Flat Lamination Bonding |
| Appearance | White / Solid |
| Component | PUR (Polyurethane) |
| Application Industry | PUR Hot Melt Adhesive for Woodworking Flat Lamination Bonding |
| Solid Content | 100 Percent |
| Operating Temperature | 130℃～140℃ |
| Melt Viscosity | Around 6500mPa·s @140℃(Brookfield-ASTM D3236) |
| Open Time | 5-6 Minutes |
| Usage Scope | Flat Lamination of Plastic Films/Aluminized Films to Wood/Wood-plastic Materials |
| Shelf Life | 6 Months |
| Package | 2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel |
FEATURE
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final bonding strength.
PUR-9002.1 has good peeling strength, good heat&moisture resistance and chemical resistance after curing.
USER GUIDE
The package method of PUR-9002.1 is suitable for various dispensing equipment.
The recommended operating temperature is 130℃~140℃.
In order to achieve complete curing, it is better to place finished products in a working environment with suitable temperature and humidity (recommended temperature: 23~25 ℃, about 65% relative humidity).
STORAGE
Store reactive PUR hot melt adhesive PUR-9002.1 where it’s dry, cool and avoid direct sunlight. The storage temperature should be no more than 35℃ and avoid open fire or heat source.