Wood Milky Flat Lamination Hot Melt Adhesives Laminating Acrylic PUR-9002S
|Place of Origin:||CHINA|
|Certification:||ISO9001 ISO14001 IATF16949|
Payment & Shipping Terms:
|Minimum Order Quantity:||20 KG|
|Packaging Details:||310ml/Aluminum Tube, 20Kg/Barrel, 200Kg/Barrel|
|Delivery Time:||5-8 work days|
|Payment Terms:||L/C, T/T|
|Product:||PUR Hot Melt Adhesive||Component:||PUR (Polyurethane)|
|Appearance:||Milky Solid||Solid Content:||100 Percent|
|Shelf Life:||Half One Year||Melt Viscosity:||9000~12000mPa·s@130℃|
|Operating Temperature:||130℃～150℃||Open Time:||3-4 Minutes @ 25℃|
|Useage Scope:||Flat Lamination Bonding Of All Kinds Of Films To All Kinds Of Boards||Application Industry:||Woodworking Flat Lamination Bonding|
wood Flat Lamination Hot Melt Adhesives,
milky Flat Lamination Hot Melt Adhesives,
hot melt laminating acrylic
Hot Sale High Quality Viscosity 9000~12000cps@130℃(Brookfield-ASTM D3236) Milky White Solid WANLI® PUR-9002S Reactive Hot Melt Adhesive for PVC / PET Films to Galvanized Sheet / MDF Board / Wood-Plastic Board / Solid Wood Board Flat Lamination Bonding Application
Wanli® PUR hot melt adhesive PUR-9002S for woodworking flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-9002S can be used for the lamination of PVC films/PET films to galvanized sheet/MDF board/wood-plastic board/solid wood board and lamination of other kinds of plates to films. PUR-9002S is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final bonding strength. After curing, PUR-9002S has good peeling strength, good heat&humidity resistance and chemical resistance.
Wanli® PUR hot melt adhesive PUR-9002S is used for woodworking flat lamination bonding. PUR-9002S can be used for the lamination of PVC films/PET films to galvanized sheet/MDF board/wood-plastic board/solid wood board and lamination of other kinds of plates to films.
|Application Material||Decorative Panels Lamination Bonding|
|Application Industry||Woodworking Flat Lamination Bonding|
|Solid Content||100 Percent|
5500~7500mPa·s@140℃ And 9000~12000mPa·s@130℃(Brookfield-ASTM D3236)
|Open Time||3-4 Minutes @ 25℃|
|Usage Scope||Flat Lamination Bonding of All Kinds of Films to All Kinds of Boards|
|Shelf Life||Half One Year|
|Package||310ml/Aluminum Tube, 20Kg/Barrel, 200Kg/Barrel|
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final bonding strength.
PUR-9002S has good peeling strength, good heat&humidity resistance and chemical resistance after curing.
The package of PUR-9002S is suitable for various dispensing equipment.
The recommended operating temperature is 130℃~150℃.
In order to achieve complete curing, it is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25 ℃, about 65% relative humidity).
Store the product where it’s dry, cool and avoid direct sunlight. The storage temperature should be no more than 35℃ and avoid open fire or heat source.