White To Light Yellow Adhesive Laminate Wood 4000 Cps PUR Hotmelt PUR-1932F
Product Details:
| Place of Origin: | CHINA |
| Brand Name: | WANLI-ADHESION |
| Certification: | ISO9001 ISO14001 IATF16949 |
| Model Number: | PUR-1932F |
Payment & Shipping Terms:
| Minimum Order Quantity: | 20 KG |
|---|---|
| Packaging Details: | 2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel |
| Delivery Time: | 5-8 work days |
| Payment Terms: | L/C, T/T |
|
Detail Information |
|||
| Product: | PUR Hot Melt Adhesive | Component: | PUR (Polyurethane) |
|---|---|---|---|
| Appearance: | White To Light Yellow / Solid | Solid Content: | 100 Percent |
| Shelf Life: | 6·Months | Melt Viscosity: | Around 4000mPa·s@140℃ |
| Operating Temperature: | 110-140℃ | Open Time: | Approximate 4 Min@25℃ |
| Usage Scope: | Flat Lamination Bonding Of Various Wood-based, Plastic, Metal And Others | Application Industry:: | PUR Hot Melt Glue For Woodworking Flat Lamination Bonding |
| High Light: | white adhesive laminate wood,light yellow adhesive laminate wood,4000 cps pur hotmelt |
||
Product Description
Factory Hot Sale WANLI® PUR-1932F White To Yellowish 100% Solid Reactive PUR Hot Melt Adhesive with High Initial Strength for PVC, PETG, PMMA, PET, Melamine Impregnated Paper And Other Surface Materials during Flooring Production
Wanli® PUR hot melt adhesive PUR-1932F for flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. Reactive polyurethane hot melt adhesive PUR-1932F has high initial strength for PVC, PETG, PMMA, pet, melamine impregnated paper and other surface materials. PUR-1932F can be used for the bonding of various wood-based, plastic, metal and other substrates. PUR-1932F is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final strength. After curing, PUR-1932F has good peel strength, good heat and humidity resistance and chemical resistance, resistant to boiling for 3 hours.
APPLICATION
Wanli® PUR hot melt adhesive PUR-1932F is used for flat lamination bonding. Reactive polyurethane hot melt adhesive PUR-1932F has high initial strength for PVC, PETG, PMMA, pet, melamine impregnated paper and other surface materials. PUR-1932F can be used for the bonding of various wood-based, plastic, metal and other substrates.
| Application Material | Woodworking Flat Lamination PUR Hot Melt Adhesives |
| Appearance | White To Light Yellow / Solid |
| Component | PUR (Polyurethane) |
| Application Industry | PUR Hot Melt Glue for Woodworking Flat Lamination Bonding |
| Solid Content | 100 Percent |
| Operating Temperature | 110-140℃ |
| Melt Viscosity | Around 4000mPa·s@140℃(Brookfield-ASTMD3236) |
| Open Time | Approximate 4 min@25℃ |
| Usage Scope | Flat Lamination Bonding of Various Wood-based, Plastic, Metal And Others |
| Shelf Life | 6·Months |
| Package | 2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel |
FEATURE
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final strength.
PUR-1932F has good peel strength, excellent heat and humidity resistance and chemical resistance after curing.
USER GUIDE
The package of PUR-1932F is suitable for various dispensing equipment.
The recommended operating temperature is 110℃~140℃.
In order to achieve complete curing, it is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, about 65% relative humidity).
STORAGE
Store Reactive polyurethane hot melt adhesive PUR-1932F where it’s dry, cool and avoid direct sunlight. The storage temperature should be no more than 35℃ and avoid open fire or heat source.