PETG PMMA Flat Lamination Hot Melt Adhesives White Polyurethane Reactive PUR-1947
|Place of Origin:||CHINA|
|Certification:||ISO9001 ISO14001 IATF16949|
Payment & Shipping Terms:
|Minimum Order Quantity:||20 KG|
|Packaging Details:||2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel|
|Delivery Time:||5-8 work days|
|Payment Terms:||L/C, T/T|
|Product:||PUR Hot Melt Adhesive||Component:||Polyurethane(PUR)|
|Appearance:||White & Solid||Solid Content:||100 %|
|Shelf Life:||6 · Months||Melt Viscosity:||About 5500mPa·s At 140℃|
|Operating Temperature:||110-150 ℃||Open Time:||About 6min At 25℃|
|Usage Scope:||Flooring Lamination Bonding Of All Kinds Of Substrates To Surface Materials||Application Industry::||Woodworking(Flooring) Flat Lamination Bonding|
petg Flat Lamination Hot Melt Adhesives,
pmma Flat Lamination Hot Melt Adhesives,
white polyurethane reactive
China Factory Promotion Flooring Flat Lamination Bonding Reactive PUR Hot Melt Glue WANLI® PUR-1947 White Solid with High Initial Strength for PVC, PETG, PMMA, PET, Melamine Impregnated Paper And Other Surface Materials
Wanli® PUR hot melt adhesive PUR-1947 for flooring flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-1947 can be used for the bonding of various wood-based, plastic, metal and other substrates. PUR-1947 has high initial strength for PVC, PETG, PMMA, pet, melamine impregnated paper and other surface materials. PUR-1947 is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final strength. After curing, PUR-1947 has good peel strength, good heat and humidity resistance and chemical resistance.
Wanli® reactive PUR hot melt adhesive PUR-1947 is used for flooring flat lamination bonding. PUR-1947 can be used for the bonding of various wood-based, plastic, metal and other substrates. PUR-1947 has high initial strength for PVC, PETG, PMMA, pet, melamine impregnated paper and other surface materials.
|Application Material||Woodworking(Flooring) Flat Lamination Hot Melt Adhesives|
|Appearance||White & Solid|
|Application Industry||Woodworking(Flooring) Flat Lamination Bonding|
|Solid Content||100 %|
|Operating Temperature||110-150 ℃|
|Melt Viscosity||About 5500mPa·s at 140℃(Brookfield-ASTMD3236)|
|Open Time||About 6min at 25℃|
|Usage Scope||Flooring Lamination Bonding of All kinds of Substrates To Surface Materials|
|Shelf Life||6 · Months|
|Package||2Kg/Bag&Carton Barrel, 20Kg/Barrel, 200Kg/Barrel|
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final strength.
PUR-1947 has good peel strength, good heat and humidity resistance and chemical resistance after curing.
The package of PUR-1947 is suitable for various dispensing equipment.
The recommended operating temperature is 110℃~150℃.
In order to achieve complete curing, it is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, about 65% relative humidity).
Store Wanli® reactive PUR hot melt adhesive PUR-1947 where it’s dry, cool and avoid direct sunlight. The storage temperature should be no more than 35℃ and avoid open fire or heat source.