Polyurethane Flat Lamination Hot Melt Adhesives 5000 Cps , Yellow PUR Adhesive PUR-886
|Place of Origin:||CHINA|
|Certification:||ISO9001 ISO14001 IATF16949|
Payment & Shipping Terms:
|Minimum Order Quantity:||20 KG|
|Packaging Details:||2Kg/Bag, 20Kg/Barrel|
|Delivery Time:||5-8 work days|
|Payment Terms:||L/C, T/T|
|Product:||PUR Hot Melt Adhesive||Component:||PUR (Polyurethane)|
|Appearance:||Yellow & Solid||Solid Content:||100 Percent|
|Shelf Life:||Half A Year||Melt Viscosity:||Around 5000mPa·s@160℃|
|Operating Temperature:||160±5℃||Open Time:||2~3 Minutes @25℃|
|Useage Scope:||Flat Lamination Bonding Of Various Wood-based, EVA Foam, PC Foam Etc.||Application Industry:||Woodworking Flat Lamination Bonding|
Polyurethane Flat Lamination Hot Melt Adhesives,
5000 cps Flat Lamination Hot Melt Adhesives,
yellow pur adhesive
China Factory Promotion Flat Lamination Bonding of Decorative Panels PUR Hot Melt Adhesive WANLI® PUR-886 with Open Time 2~3 Minutes @25℃ And Good Peel Strength, Excellent Heat & Moisture & Chemical Resistance
Wanli® PUR hot melt adhesive PUR-886 for flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-886 can be used for the bonding of various wood base, EVA foam, PC foam and other substrates. PUR-886 has higher initial strength for PVC, leather, veneer, PET , melamine impregnated paper and other surface materials. PUR-886 is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final strength. After curing, PUR-886 has good peel strength, good heat and humidity resistance and chemical resistance.
Wanli® PUR hot melt adhesive PUR-886 is used for flat lamination bonding. PUR-886 can be used for the bonding of various wood base, EVA foam, PC foam and other substrates. PUR-886 has higher initial strength for PVC, leather, veneer, PET , melamine impregnated paper and other surface materials.
|Application Material||Woodworking Flat Lamination Hot Melt Adhesives|
|Appearance||Yellow & Solid|
|Application Industry||Woodworking Flat Lamination Bonding|
|Solid Content||100 Percent|
|Melt Viscosity||Around 5000mPa·s@160℃(Brookfield-ASTMD3236)|
|Open Time||2~3 Minutes @25℃|
|Usage Scope||Flat Lamination Bonding of Various Wood-based, EVA Foam, PC Foam etc.|
|Shelf Life||Half A Year|
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final strength.
PUR-886 has good peel strength, good heat and humidity resistance and chemical resistance after curing.
The package of PUR-886 is suitable for various dispensing equipment.
The recommended operating temperature is 160±5℃.
In order to achieve complete curing, it is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, about 65% relative humidity).
Store the product where it’s dry, cool and avoid direct sunlight. The storage temperature should be no more than 35℃ and avoid open fire or heat source.