Flat Lamination PUR Hot Melt Adhesive Solid HMA Glue PUR-886
|Place of Origin:||CHINA|
|Certification:||ISO9001 ISO14001 IATF16949|
Payment & Shipping Terms:
|Minimum Order Quantity:||20 KG|
|Packaging Details:||2Kg/Bag, 20Kg/Barrel|
|Delivery Time:||5-8 work days|
|Payment Terms:||L/C, T/T|
|Product:||PUR Hot Melt Adhesive||Component:||PUR (Polyurethane)|
|Appearance:||Yellow Solid||Solid Content:||100%|
|Shelf Life:||Half One Year||Melt Viscosity:||About 5000mPa·s @160℃|
|Operating Temperature:||160±5℃||Open Time:||2~3min@25℃|
|Useage Scope:||Flat Lamination Bonding Of Various Wood-based, EVA Foam, PC Foam Etc.||Application Industry:||Woodworking Flat Lamination Bonding|
flat PUR hot melt adhesive,
Lamination PUR hot melt adhesive,
solid hma glue
Good Quality Factory Directly Yellow Solid PUR(Polyurethane) Hot Melt Adhesive WANLI® PUR-886 with Operating Temperature 160±5℃ for Flat Lamination Bonding of Various Wood Base, EVA Foam, PC Foam And Other Substrates
Wanli® PUR hot melt adhesive PUR-886 for flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-886 can be used for the bonding of various wood base, EVA foam, PC foam and other substrates. PUR-886 has higher initial strength for PVC, leather, veneer, PET , melamine impregnated paper and other surface materials. PUR-886 is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final strength. After curing, PUR-886 has good peel strength, good heat and humidity resistance and chemical resistance..
Wanli® PUR hot melt adhesive PUR-886 is used for flat lamination bonding. PUR-886 can be used for the bonding of various wood base, EVA foam, PC foam and other substrates. PUR-886 has higher initial strength for PVC, leather, veneer, PET , melamine impregnated paper and other surface materials.
|Application Material||Woodworking Flat Lamination Hot Melt Adhesives|
|Application Industry||Woodworking Flat Lamination Bonding|
|Operating Temperature||160±5℃( Depend On Equipment, Substrate, Environment And Other Conditions)|
|Melt Viscosity||About 5000mPa·s@160℃(Brookfield-ASTMD3236)|
|Usage Scope||Flat Lamination Bonding of Various Wood-based, EVA Foam, PC Foam etc.|
|Shelf Life||Half One Year|
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final strength.
PUR-886 has good peel strength, good heat and humidity resistance and chemical resistance after curing.
The package of PUR-886 is suitable for various dispensing equipment.
The recommended operating temperature is 160±5℃.
It is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, about 65% relative humidity) to achieve complete curing.
Dry, cool, avoid direct sunlight, no more than 35℃.