5500 To 7500 Cps Polyurethane Hot Melt Glue Lamination For Decorative Panels PUR-9002S
|Place of Origin:||CHINA|
|Certification:||ISO9001 ISO14001 IATF16949|
Payment & Shipping Terms:
|Minimum Order Quantity:||20 KG|
|Packaging Details:||310ml/Aluminum Tube, 20Kg/Barrel, 200Kg/Barrel|
|Delivery Time:||5-8 work days|
|Payment Terms:||L/C, T/T|
|Product:||PUR Hot Melt Adhesive||Component:||PUR (Polyurethane)|
|Appearance:||Milky White & Solid||Solid Content:||100%|
|Shelf Life:||6 Months||Melt Viscosity:||5500~7500cps@ 140℃|
|Operating Temperature:||130～ 150 ℃||Open Time:||3-4 Min @ 25℃|
|Useage Scope:||Flat Lamination Of All Kinds Of Films To All Kinds Of Boards||Application Industry:||Woodworking Flat Lamination Bonding|
5500 cps polyurethane hot melt glue,
7500 cps polyurethane hot melt glue,
lamination glue hot melt
Factory Direct High Quality PUR(Polyurethane) Reactive Hot Melt Adhesive WANLI® PUR-9002S with Viscosity 5500~7500cps@140℃(Brookfield-ASTM D3236) for Flat Lamination Bonding of All Kinds of Films to All Kinds of Boards
Wanli® PUR hot melt adhesive PUR-9002S for woodworking flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-9002S can be used for the lamination of PVC films/PET films to galvanized sheet/MDF board/wood-plastic board/solid wood board and lamination of other kinds of plates to films. PUR-9002S is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final bonding strength. After curing, PUR-9002S has good peeling strength, good heat&humidity resistance and chemical resistance.
Wanli® PUR hot melt adhesive PUR-9002S is used for woodworking flat lamination bonding. PUR-9002S can be used for the lamination of PVC films/PET films to galvanized sheet/MDF board/wood-plastic board/solid wood board and lamination of other kinds of plates to films.
|Application Material||Decorative Panels Lamination Bonding|
|Appearance||Milky White & Solid|
|Application Industry||Woodworking Flat Lamination Bonding|
|Operating Temperature||130～150 ℃( Depend On Equipment, Substrate, Environment And Other Conditions)|
|Open Time||3-4 min @ 25℃|
|Usage Scope||Flat Lamination of All Kinds of Films to All Kinds of Boards|
|Shelf Life||6 Months|
|Package||310ml/Aluminum Tube, 20Kg/Steel Barrel, 200Kg/Steel Barrel|
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final bonding strength.
PUR-9002S has good peeling strength, good heat&humidity resistance and chemical resistance after curing.
The package of PUR-9002S is suitable for various dispensing equipment.
The recommended operating temperature is 130℃~150℃.
It is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25 ℃, about 65% relative humidity) to achieve complete curing.
Dry, cool, avoid direct sunlight, no more than 35℃.