PUR Solid Textile Adhesive Glue Lamination For Polyester Fabric PUR-4100C
|Place of Origin:||CHINA|
|Certification:||ISO9001 ISO14001 IATF16949|
Payment & Shipping Terms:
|Minimum Order Quantity:||20 KG|
|Packaging Details:||2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel|
|Delivery Time:||5-8 work days|
|Payment Terms:||L/C, T/T|
|Product:||PUR Hot Melt Adhesive||Component:||PUR (Polyurethane)|
|Appearance:||Light-Yellow Solid||Solid Content:||100 %|
|Shelf Life:||6 (Months)||Melt Viscosity:||Around 4500 MPa·s @ 90 ℃|
|Operating Temperature:||90~110 ℃||Useage Scope:||Fabric To Film Bonding|
|Application Industry:||Textile Lamination Bonding|
PUR Textile Adhesive Glue,
solid Textile Adhesive Glue,
lamination adhesive for polyester fabric
Best Selling Lamination of Membrane and Functional Textiles Hot Melt Adhesives PUR-4100C with Innovative Design
Wanli® PUR hot melt adhesive PUR-4100C for textile lamination bonding is a one-component reactive PUR hot melt adhesive with 100% solids.PUR-4100C can be used on a wide variety of fabrics and different plastic films. The end product is hard with good initial strength, moderate open time and excellent final strength. PUR-4100C is characterized by stable viscosity when heated at a certain temperature and high initial and final bond strength. PUR-4100C has good peel strength, good heat and moisture resistance and chemical resistance after curing.
Wanli® PUR hot melt adhesive PUR-4100C is used for textile lamination bonding. PUR-4100C can be used for all kinds of fabrics and different plastic films. The final product is stiff, with good initial strength, moderate opening time and excellent final strength.
|Application Material||Fabric to Film Lamination Bonding|
|Appearance||Light Yellow Solid|
|Application Industry||Textile Lamination Bonding|
|Melt Viscosity||About 4500mPa·s at 90℃(Brookfield-ASTMD3236)|
|Usage Scope||Fabric to Film Bonding|
|Shelf Life||6 Months|
|Package||2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel|
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final bonding strength.
After curing, PUR-4100C has good peeling strength, good heat&humidity resistance and chemical resistance.
The package of PUR-4100C is suitable for various dispensing equipment.
The recommended operating temperature is 90℃~110℃.
In order to achieve complete curing, it is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, about 65% relative humidity).
Store PUR-4100C where it’s dry, cool and avoid direct sunlight. The storage temperature should be no more than 35℃ and avoid open fire or heat source.