Distinctive 2KPU-802 Polyurethane Adhesive 700 MPa.S
|Place of Origin:||CHINA|
|Certification:||ISO9001 ISO14001 IATF16949|
Payment & Shipping Terms:
|Minimum Order Quantity:||18KG|
|Packaging Details:||18/18kg Barrel|
|Delivery Time:||5-8 work days|
|Payment Terms:||L/C, T/T|
|Appearance:||A: Dark Amber Liquid/B: Light To Colorless Liquid||Density:||A: 0.97(g/cm3)/B: 1.13(g/cm3)|
|Viscosity:||A: 1600±300(mPa.s)/B:200±100(mPa.s)||Weight Mixing Ratio:||A: 100/B: 100|
|Mixed Viscosity:||400-700 (mPa.s)||Application Period:||4~6(minutes)|
|Hardness:||90-99 (Shore A)||Shear Strength:||ABS: 2.22 (MPa), UPVC: 2.72 (MPa)|
Distinctive 2K Polyurethane Adhesive,
2K Polyurethane Adhesive 700 mPa.s,
99 Shore A 2K Polyurethane Adhesive
Wanli® 2KPU-802 is used for fast adhesive sealing of hollow fibre filters for water treatment applications.
|Appearance||Dark amber liquid||Light to colorless liquid|
|Weight Mixing Ratio||100||100|
|Hardness (Shore A)||90-99|
|Shear Strength (MPa)||ABS:2.22, UPVC:2.72|
|Shelf Life||12 Months||6 Months|
It has excellent resistance to hydrolysis, acid, alkali and oxidation. Suitable for dynamic mixing and filling processes.
Surface treatment: Clean the surface of the material to be adhered to ensure that it is dry, clean and free from oily contaminants. For film with a high water content, air bubbles may be produced.
Glue preparation: A/B components are mixed evenly according to the weight ratio A:B=1:1, it is recommended to use automatic glue mixing equipment, if manual glue mixing is used, it is recommended to use after defoaming, defoaming and glue application must be completed within the applicable period.
Curing: After curing at room temperature for 30 minutes, the product can be processed in the next process.
Store in a cool, dry environment and out of direct sunlight. Store at a temperature of 8 °C to 28 °C and away from fire and heat sources. Under the storage conditions described above, this gel A can be stored for 12 months and gel B for 6 months.